Carbon Black N339, China Carbon Black Manufacturer & Supplier
Carbon Black N339 is used in the tread compounds of passenger tire and truck tire, coating compounds of conveyor belt, hose and industrial compounds and also Printing inks
Carbon Black N339
Other Name:High Abrasion Furnace Black-high Structure （New technology）；HAF-HS（New technology）
Compared to N330, N339 has higher structure, smaller particles.
The N339 compound has better abrasion and crack resistance than those of high abrasion furnace black –high structure (old technology) such as N347.
Application:
N339 is used in the tread compounds of passenger tire and truck tire, coating compounds of conveyor belt, hose and industrial compounds with high abrasion properties.
It is also used in Printing Inks.
Usage:
The tread compound filled with N339 has similar re-inforcement, abrasion and crack resistance properties as those of Carbon Black N220 compounds, and has good extrusion property, very suitable for butyl benzene rubber/ butyl rubber compound.
The N339 compound has the highest rolling resistance among all the compounds with N330 series.
| CARBON BLACK N339 | |||
| Iodine Adsorption No | g/kg | 90±7 | |
| CTAB Absorption No Specific Surface Area | 103m2/kg | 84~102 | |
| Nitrogen Adsorption Specific Surface Area | 103m2/kg | 84~98 | |
| STSA | 103m2/kg | 88±9 | |
| DBP Absorption No | 10-5m3/kg | 120±7 | |
| DBP Absorption No (compress sample) | 10-5m3/kg | 91~107 | |
| Tint Strength | % | 103~119 | |
| Heating Loss | % | ≤ | 2.5 |
| Ash content | % | ≤ | 0.5 |
| Pour Density | kg/m3 | 345±40 | |
| Fines | % | ≤ | 10 |
| PH | 5~9 | ||
| Impurity | NONE | ||
| 45um Sieve Residue | % | ≤ | 0.1 |
| 500um Sieve Residue | % | ≤ | 0.001 |
| Stress at 300% Elongation | Mpa | 0.6±1.6 |